Laser fusion brazing welding was proposed.Galvanized steel/AA6061 lapped joint was obtained by laser fusion brazing welding technique using the laser-induced aluminium molten pool spreading and wetting the solid steel surface.Wide joint interface was formed using the rectangular laser beam coupled with the synchronous powder feeding.The result showed that the tiny structure with the composition of a-Al and Al–Si eutectic was formed in the weld close to the Al side.And close to the steel side,a layer of compact Fe–Al–Si intermetallics,including the Al-rich FeAl3,Fe2Al5 phases and Al–Fe–Si s1 phase,was generated with the thickness of about 10–20 lm.Transverse tensile shows the brittlefractured characteristic along to the seam/steel interface with the maximum yield strength of 152.5 MPa due to the existence of hardening phases s1 and Al–Fe intermetallics.
Laser fusion brazing welding was proposed. Galvanized steel / AA6061 lapped joint was obtained by laser fusion brazing welding technique using the laser-induced molten pool spreading and wetting the solid steel surface. Width joint surface was formed using the rectangular laser beam coupled with the synchronous powder feeding. The result showed that the tiny structure with the composition of a-Al and Al-Si eutectic was formed in the weld close to the Al side. And close to the steel side, a layer of compact Fe-Al-Si intermetallics, including the Al-rich FeAl3, Fe2Al5 phases and Al-Fe-Si s1 phase, was generated with the thickness of about 10-20 lm. Transverse tensile shows the brittle fracture characteristic along to the seam / steel interface with the maximum yield strength of 152.5 MPa due to the existence of hardening phases s1 and Al-Fe intermetallics.