通过研究爆轰波形的控制机理,分析指出其在实际工程应用中的相关注意事项。采用两种不同工艺方案对大面积钛/钢复合板进行爆炸焊接实验。接着对制备的TA1/Q345R爆炸复合试样进行宏观形貌、力学性能、微观组织等分析。结果表明:采用分段装药工艺所制备的钛/钢复合板界面无熔化、鼓棱、撕裂、剪切强度低等缺陷,相关性能检测满足NB/T47002.3-2009标准,能够满足装备实验需求。 By studying the control mechanism of detonation wave, the relevant precautions in practical engineering application are pointed out. Two different process schemes were used to conduct the explosion welding experiments on a large area of ​​titanium / steel composite plates. Then the prepared TA1 / Q345R explosive composite samples were macro-morphology, mechanical properties, microstructure and other analysis. The results show that the interface of titanium / steel composite plate prepared by the segmented charge process has no defects such as melting, drum edge, tearing and low shear strength, and the related performance testing meets the criteria of NB / T47002.3-2009 to meet the requirement of equipment Experimental needs.