Single crystal of dysprosium-doped yttrium aluminum tetraborate Dy:YAl3(BO3)4(Dy:YAB) was grown by the flux method. The room-temperature absorption spectrum and
Cordierite-based glass-ceramics with non-stoichiometric composition doped with rare earth oxide (REO2) and heavy metal oxide (M2O3) respectively were fabricated