本文利用X射线方法测定18.36%Zn α黄铜的层错能,其结果为:利用谱线变 宽效应得出∈=9.74尔格/厘米~2,利用谱线位移效应得出∈=10.95尔格 /厘米,这些结果与Smallman(1957)的符合得很好。
In this paper, the X-ray method was used to determine the layer-fault energy of 18.36% Zn α brass. The results show that ε = 9.74 erg / cm ~ 2 is obtained by the line widening effect, Cm, these results in good agreement with Smallman (1957).