NONDESTRUCTIVE BAND-GAP PROFILE DETERMINATION OF HgCdTe LPE GROWN LAYERS

来源 :红外与毫米波学报 | 被引量 : 0次 | 上传用户:chiyulong2000
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Infrared transmission and photoconductivity spectra of mercury-cadmium telluride (MCT) epitaxial layers,grown by liquid phase epitaxy (LPE) on CdTe and CdZnTe wide band-gap substrates,were investigated both theoretically and experimentally at temperatures T=82 K and T=300 K in the infrared (IR) wavelength region 3-15 μm.The photoresponse position of the diodes was determined at cryogenic temperatures from the transmission spectra of room temperature.Theoretical calculations of optical density D(h-ω),needed for analysis of experimental optical transmission data,were performed in the framework of WKB approximation.
其他文献
通过差示扫描量热技术,研究了热循环对Cu-23.6Zn-4.47Al-0.23Mn-0.17Ni形状记忆合金中双可逆相变的影响.结果表明,X→M转变温度随热循环的进行而降低,而马氏体逆转变的温度几
采用连续波 2 k W YAG激光器在 6 0 6 1铝合金表面激光熔覆 Ni Cr BSi合金。利用扫描电子显微镜 (SEM/EDX)、X射线衍射仪等分析检测设备研究熔覆层的组织形貌、化学成分及相
通过等温压缩试验和金相分析研究了热变形参数对 Ti-15-3(Ti-15V-3Cr-3Sn-3Al)合金固溶处理后显微组织的影响.等效晶粒尺寸随变形温度升高而增大、随变形程度和变形速率增加而减小:再结晶程度随变形温度升
采用光电子能谱分析方法对掺杂 L a2 O3的 Mo粉的性能进行了研究。结果表明 :掺杂 L a(NO3) 3的 Mo O2 粉经过还原处理后 ,Mo粉表面的纳米 L a2 O3微粒可以减小 Mo基体的特征
以 2 0 90铝锂合金为对象 ,研究了稀土元素 Ce和预变形对其时效过程的影响。结果表明 :微量 Ce(0 .11% )能显著弥散 T1 相 ,使 T1 相均匀、细小地析出 ,且在峰时效态表现明显
通过实验俭测和数值模拟方法研究结晶器切缝形式、弯月面位置以及感应线圈匝数等因素对方坯软接触电磁连铸结晶器内高频磁场分布的影响.分析结果表明:采用通体切缝形式的结晶器
王军是河北人,现年46岁,高中毕业后到县医药公司工作。由于近年来药店遍地开花,公司效益越来越差,为了实现买房买车让家人过上衣食无忧的日子,他决定辞职自闯一番事业,在网上
在旋转圆盘仪多相流损伤实验中,NiTi合金表现出十分良好的抗冲刷磨损及空蚀和冲刷磨损联合作用性能,拉伸和循环应力-应变力学测量表明,NiTi合金具有类橡皮弹性吸收能量的相变伪弹性特点 ,
环境与健康是环境卫生工作的主题,其实质是环境污染造成环境质量恶化而产生一系列健康问题.随着经济的不断发展,居民生活水平的不断提高,对环境卫生的要求越来越高.目前我国
本文利用岛津UV3101-PC分光光度计,测定了云母1/4波片的偏振干涉谱.该光谱和以往文献中的显著不同.本文对此进行了分析和解释,并由此得出了在考虑吸收的情况下的爱里方程表达