The hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 ℃ and strain rates of 0.01-10 s-1.The effects of Cu addition and different deformation parameters on defo
【机 构】
:
Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
论文部分内容阅读
The hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 ℃ and strain rates of 0.01-10 s-1.The effects of Cu addition and different deformation parameters on deformation behavior were,respectively,characterized by analyzing flow curves,constitutive equations and microstructures.The results indicated that the shapes of flow curves strongly depended on the volume fraction of two phases.When deformed at low strain rate,DRV in ferrite was prompted with increase in the temperature and was further developed to continuous DRX.At high strain rate,flow localization preferentially occurred in ferrite at low deformation temperature due to the strain partitioning and relatively less fraction of ferrite.The activation energy for 2205-Cu DSS was 452 kJ/mol and was found to connect with the variation of strain,strain rate and deformation temperature.The optimum hot deformation parameters for 2205-Cu DSS were obtained in the temperature range of 1100-1150 ℃ and strain rate range of 0.1-1 s-1 with a peak power dissipation efficiency of 41%.Flow localization was the main way to lead to flow instability.Meanwhile,the Cu-rich precipitates were generated within a few ferrite grains when deformed at temperature lower than 1000 ℃.The interaction between dislocations and Cu-rich precipitates at high strain rate,as well as the limited DRV in ferrite and DRX in austenite,contributed to the complex microstructure and flow behavior.
其他文献
Microstructure and mechanical properties of Ni-28W-6Cr alloy-welded joints produced by gas tungsten arc welding were investigated in this work.Results showed that original fine-grain base metal near fusion line totally transformed into coarse heat affecte
Immiscible alloys have aroused considerable interests in the last decades on account of their special physical and mechanical properties and potential applications.A considerable number of researches have been implemented to investigate the solidification
Hot deformation behavior of a high Al-low Si transformation-induced plasticity (TRIP) steel was studied by an MMS-300 thermo-simulation machine at the temperature range of 1050-1200 ℃ and strain rate range of 0.01-10 s-1.The constitutive equations of the
In a fusion reactor,plasma-facing components (PFCs) will suffer severe thermal shock;behavior and performance of PFCs under high heat flux (HHF) loads are of major importance for the long-term stable operation of the reactor.This work investigates the the
The composition and structural evolution of the corrosion product film of two commercial 90Cu-10Ni tubes,namely Tube A and Tube B,after being immersed in natural seawater for 1,3,and 6 months were characterized by scanning electron microscopy,energy-dispe
The effect of thermal aging on phase transformation and impact toughness of an as-cast duplex stainless steel was investigated at room temperature.After long-term thermal aging,the impact toughness decreases significantly and the cracks initiate and propa
The fracture of pipelines caused by corrosion cracks and the resulting oil and gas leakage can lead to great environmental pollution and economic losses.These negative effects are due to serious corrosion of the plain carbon steels used for armor of flexi
The strain rate sensitivity (SRS) and temperature sensitivity (TS) of 316L austenitic stainless steel were investigated by constant strain rate test (CSRT) and strain rate jump test (SRJT) under four temperatures (293,373,473 and 573 K) and four strain ra
Three-dimensional parts of the 30CrMnSiA steel were successfully fabricated using selective laser melting (SLM).The microstructures and mechanical properties of the SLM-processed 30CrMnSiA samples were investigated by scanning electron microscope and tran
The crevice corrosion behaviors of 436 stainless steels in chloride-containing solutions with sulfate addition were studied using potentiodynamic,galvanostatic and repassivation potential measurements.The results of these electrochemical tests were compar