By careful design of rolling schedule,ultra-fine (~2μm) ferrite grains in a low carbon high niobium (0.09wt%Nb) micro-alloying steel with average austenite grain sizes above 800 μm can be achieved in the simulated thin slab direct rolling process. The 5-p