论文部分内容阅读
We demonstrate that power recycling is feasible by using a semi-transparent stripped Al electrode as interconnecting layer to merge a white organic light-emitting devices(WOLED)and an organic photovoltaic(OPV)cell.The device is called a PVOLED..It has a glass/ITO/CuPc/m-MTDATA:V2O5/NPB/CBP:FIrpic:DCJTB/ BPhen/LiF/Al/P3HT:PCBM/V2O5/Al structure.The power recycling efficiency of 10.133% is achieved under the WOLED of PVOLED operated at 9 V and at a brightness of 2 110 cd/m2,when the conversion efficiency of OPV is 2.3%.We have found that the power recycling efficiency is decreased under high brightness and high applied voltage due to an increase input power of WOLED.High efficiency(18.3 cd/A)and high contrast ratio(9.3)were obtained at the device operated at 2 500 cd/m2 under an ambient illumination of 24 000 lx.Reasonable white light emission with Commission Internationale De L'Eclairage(CIE)color coordinates of(0.32,0.44)at 20 mA/cm2 and slight color shift occurred in spite of a high current density of 50 mA/cm2.The proposed PVOLED is highly promising for use in outdoors display applications.