将金属玻璃Fe_(40)Ni_(40)P_(12)B_8薄带进行20min等时横磁和横磁张力退火,测定了13至130℃的感生磁各向异性。磁化感生各向异性K_(um)涉及窄的激活能分布,激活能约1.4eV。K_
论文部分内容阅读
将金属玻璃Fe_(40)Ni_(40)P_(12)B_8薄带进行20min等时横磁和横磁张力退火,测定了13至130℃的感生磁各向异性。磁化感生各向异性K_(um)涉及窄的激活能分布,激活能约1.4eV。K_(um)的温度依赖性遵从关系K_(um)(T)∝M_s~(α_m)(T),其中α_m近似为2.3。应变感生各向异性K_(us)具有正值,在类似关系式中的相应指数α_s可比2甚大。
The transverse magnetic and transverse magnetic tension anneals of the Fe 40 Ni 40 P 12 B 8 ribbons were carried out for 20 min, and the induced magnetic anisotropy was measured at 13 to 130 ℃. Magnetization Anisotropy K_ (um) relates to a narrow activation energy distribution with an activation energy of about 1.4 eV. The temperature dependence of K_ (um) obeys the relation K_ (um) (T) αM_s ~ (α_m) (T), where α_m is approximately 2.3. The strain-induced anisotropy K_ (us) has a positive value, and the corresponding index α_s in a similar relationship can be larger than 2.
其他文献
1975年6月 日本复合材料学会成立 首任会长林毅上任 10月 日文版《日本复合材料学会志》创刊(季刊) 11月 召开第一届复合材料讨论会(东京大学工学部)
June 1975 The first
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
近20年来非金属复合材料被称为未来的航空航天材料。如今,复合材料的广泛应用并非在民用飞机的表面控制和承载结构方面、军用飞机原有结构的强度、刚度、隐身超越控制方面取
粉末的特性可通过合金的可硬化能力、粉粒的形状和可压缩性来影响零件强度与功能.最近,在基体合金方面已出现了许多变化。由于汽车工业不断强调减轻重量,所以在许多应用方面
吴羽化学工业和三岛制纸公司,共同研制了含碳纤维导电性薄膜,并已开始用Kvrepeam商品名销售。这是以碳纤维和聚乙烯浆料为原料,表面电阻率为10~4-10~2Ω的导电性优良,均匀性
在粉末荧光材料的生产中要特别注意粒度大小的分布,只要用适当的方法就能制备出非常均匀的ZnS和(Zn,Cd)S球形颗粒,这种材料是从水溶液中均相沉淀出来的。在合成过程中要严格
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
本工作研究了Bi_(2-x)Pb_xSr_2Ca_2Cu_3O_2和Bi_(1.6)Pb_(0.4-x-y)Sb_xSn_ySr_2Ca_2Cu_3O_2系统样品的超导性质。以较短的烧结时间制得零电阻温度为107K的Bi_(1.6)Pb_(0.4)Sr
制得了一类新型的热稳定性光敏聚合物。在这一类聚合物中有对光不稳定的芳族酰胺键。这些聚合物能用于平版印刷凹凸图象,在微型电路制作中用作蚀刻掩模、以及用作光信息存储
过去,采用膜分离技术制备富氧空气有两种方法。一种是用聚乙烯、聚苯乙烯或者聚乙烯对苯二甲酸酯等聚合体制成中空纤维的方法。一种是利用有机聚硅氧烷—聚碳酸酯等制成极薄