The oxidation behavior of Al2O3-30%TiCN-0.2%Y2O3 composite and its effect on high temperature bending strength was studied. The result indicates that the mass g
By using CALPHAD (Calculation of Phase Diagram) technique the optimization and calculation of the binary systems of TbCl3-ACl (A= Li, Na, K, Rb, Cs) were carrie
Bis (methylcyclopentadienyl) lanthanide amido complex (MeCp)2YbNPh2 (THF) reacted with n-hexyl isocyanate (n-HexylNCO) in 1:1 molar ratio to give {(MeC5H4)2Yb[O
Ce0.6Zr0.4O2 solid solution ultrafine particle was prepared in the cyclohexane/water/OP-10/n-hexanol reversed microemulsion. The quasi-ternary phase diagram inv
Ca8Mg(SiO4)4Cl2:Eu2+ phosphor doped with Sr2+ cation for Ca2+ partially, was synthesized by solid-state reaction at high temperature under reducing atmosphere,