<正>Ramie cloth/UP resin composite was formed at 0.2 MPa and cured at room temperature for 24 h and treated at 80℃for 2 h. The physical and mechanical properti
<正>The oxidation behaviors of bulk Ti3Si(1-x)AlxC2 prepared by hot pressing were investigated. The results show that the isothermal oxidation behavior of Ti3Si