In this work, ultrasonic fatigue behavior of the Ti40Zr10Cu34Pd14Sn2 glassy alloy was investigated at 20 kHz at a stress ratio of R = -1. The number of cycles to failure in the S-N curve obtained in this work did not decrease again even after 107 - 108 cy