【摘 要】
：
In this work,a facile route using a simple solvothennal reaction and sequential heat treatment process to prepare porous Y2O3 microcubes is presented.The as-syn
【机 构】
：
Department of Chemistry and Life Sciences,Division of Nanomaterials and Chemistry. Hefei National La
【基金项目】
：
the China Postdoctoral Science Foundation;the Natural Science Foundation of Jiangxi Province
论文部分内容阅读
In this work,a facile route using a simple solvothennal reaction and sequential heat treatment process to prepare porous Y2O3 microcubes is presented.The as-synthesized products were characterized by X-ray powder diffraction (XRD),scanning electronic microscope (SEM),energy dispersive spectrometer (EDS),thermogravimetric analysis (TG),and differential thermal analysis (DTA).The thermal decomposition process of the Y2O3 precursor was investigated.SEM results demonstrated that the as-prepared porous Y2O3 microcubes were with an average width of about 20 μm and thickness of about 8 μm.It was found that the morphology of the Y2O3 precursor could be readily tuned by varying the molar ratio of S2O28- to y3+.Y2O3:Eu3+(6.6％) microcubes were also prepared and their photoluminescence properties were investigated.
其他文献
输电网规划设计的电网工程全寿命周期成本分析可以使得电网项目在实现全寿命周期内经济、社会、环境等成本最低，综合效益最优，具有全系统、全费用、全过程，即"三全"的特点。本文
A reproducing kernel collocation method based on strong formulation is introduced for transient dynamics. To study the stability property of this method, an alg
The selective catalytic reduction reaction belongs to the gas-solid multiphase reaction,and the adsorption of NH3 and NO on CuO/y-Al2O3 catalysts plays an impor
±800kV楚雄换流站SVC装置调试阶段发现TCR电抗器运行产生的磁场，严重影响到其周围设备的安全运行，为解除隐患采取了地网解环和抬高电抗器的措施。本文对采取的措施和实施效果
The synthesis of Al2O3-coated and uncoated LiMn2O4 by solid-state method and fabrication of LiMn2O4/graphite battery were described.The structure and morphology
The microstructural evolution and interfacial reaction of the Au/Sn/Au/Sn/Au/Sn/Au couples were investigated during annealing at 453,523,and 543 K for up to 240
The microstructure of the as-cast 7A55 aluminum alloy and its evolution during homogenization were investigated by means of optical microscopy (OM),scanning ele
In order to verify the validity of finite element numerical simulation method for asphalt mixture,which consists of aggregates,mastic (where mastic is a kind of
The polycrystalline samples of Pr0.45(Ca1-xSrx)0.55MnO3 (x =0.0,0.2,0.4,0.6) were prepared by solid-state reaction.Influence of Sr2+ substitution for Ca2+ at A
To denoise the diffusion weighted images (DWIs) featured as multi-boundary,which was very important for the calculation of accurate DTIs (diffusion tensor magne