本文报导在Ni电极上化学修饰Ni[Fe(CN)_6]~(2-/1-)膜的形成过程中,支持电解质阳离子对膜的复盖度的影响。这种影响,主要是由于阳离子在Ni[Fe(CN)_6]~(2-/1-)电极上不同程度的特性吸附所引起的,经研究发现,膜的稳定性还与支持电解质阳离子的种类有关。
This paper reports the effect of supporting electrolyte cations on the coverage of the film during the formation of chemically-modified Ni [Fe (CN) 6] 2- (2- / 1-) films on Ni electrodes. This effect is mainly due to the different degree of adsorption of cations on Ni [Fe (CN) 6] 2- (1- / 1) electrode. It has been found that the stability of the membrane is also related to the support of electrolyte cations Type related.