【摘 要】
:
Growth of SiCGe ternary alloy on 6H-SiC in a conventional hot-wall CVD system was initially studied. SiH4, GeH4 and C3H8 were employed as silicon, germanium and
【机 构】
:
Department of Electronic Engineering
论文部分内容阅读
Growth of SiCGe ternary alloy on 6H-SiC in a conventional hot-wall CVD system was initially studied. SiH4, GeH4 and C3H8 were employed as silicon, germanium and carbon source, respectively, while H2 was employed as the carrier gas. To reduce the heavy lattice mismatch between the film and the substrate, a 3C-SiC buffer layer was inserted between them in a CVD process. Optimizing the growth conditions was discussed. The samples were measured by means of SEM, SAXRD (Small Angle X-Ray Diffraction). It is shown that use of the 3C-SiC buffer layer is an effective way to improve the quality of the ternary alloy.
其他文献
Extraction of o-aminophenol (OAP) using trialkylphosphine oxide (TRPO) was studied with different diluents.The neutral OAP was extracted using TRPO under an equ
The mechanical properties of LA40 magnesium alloy were investigated under compression at room temperature. In the applied strain rate range from 1.33×10-4 s-1
The crystallization behavior and mechanical properties of CaO-Al2O3-SiO2 (CAS) system glass-ceramics with addition of Y2O3 were investigated. The optimal sinter
The decomposed process of bastnaesite, monazite and mixed rare earth concentrate in CaO-CaCl-CaCl2 was studied by means of TG-DTA method. The relationship among
Based on a novel high strength Al-Cu-Li-X alloy-2A97, the effect of T6I6 and its modified processes on the properties investigated by SEM and tensile test. The
Single phase chromium-substituted orthorhombic LiMn1-xCrxO2 (0≤x≤0.05) were successfully synthesized by hydrothermal treatment of Mn2O3, Cr2O3 and lithium hyd
The effect of rectangle wave pulse current on solidification structure of ZA27 alloy was studied.The results show that the wave pattern relies on the frequency
The Al-based alloy with equiaxed grains was directly produced in the industrial aluminum electrolyzer. The varieties of grain features and grain sizes vs the re
The electrical properties of La0.6Sr0.4Co1-yFeyO3 (LSCF, y=0-1.0) cathode materials were measured by DC four probes, X-ray photo-electron spectrum (XPS) was als
Golden yellow cerium conversion film was obtained on magnesium alloys surface by immersion method and the preparation parameters were established. The influence