研制了TiSnO2+Sb2O3/PbO2金属阳极,用SEM,XRD,EDS对阳极表层进行了观测和分析。测定了在80℃,1mol·L-1\H2SO4中该电极的使用寿命和电化学动力学参数,并与贵金属及其合金电极进行了比较,采用双位垒模型讨论了该电极的电化学性能。结果表明,该电极是一种寿命长,催化活性好的非贵金属放氧阳极材料。
The TiSnO2 + Sb2O3 / PbO2 metal anode was developed. The surface of the anode was observed and analyzed by SEM, XRD and EDS. The service life and electrochemical kinetics parameters of the electrode in 1 mol·L-1H2SO4 at 80 ℃ were measured and compared with that of the noble metal and its alloy electrode. The electrochemical performance of the electrode was discussed by double-barrier model . The results show that the electrode is a long life, good catalytic activity of non-noble metal oxygen anode material.