采用气压浸渗法实现了SiC/Al和SiO2构件的原位连接,SiC/Al复合材料组织浸渗致密,SiC颗粒的分布较均匀。该复合材料的主要断裂机制为基体和颗粒的混合断裂。SiC/Al和SiO2构件
【机 构】
:
西北工业大学凝固技术国家重点实验室,
论文部分内容阅读
采用气压浸渗法实现了SiC/Al和SiO2构件的原位连接,SiC/Al复合材料组织浸渗致密,SiC颗粒的分布较均匀。该复合材料的主要断裂机制为基体和颗粒的混合断裂。SiC/Al和SiO2构件在界面处发生了反应,主要生成了Al2O3和Si。SiC/Al/SiO2的抗弯强度随保温时间的增加而增加,10 min为最佳的保温时间。
In-situ connection of SiC / Al and SiO2 was achieved by pressure impregnation. The microstructure of SiC / Al composites was infiltrated and dense, and the distribution of SiC particles was more uniform. The main fracture mechanism of the composites is mixed fracture of matrix and particles. The SiC / Al and SiO2 components reacted at the interface and mainly formed Al2O3 and Si. The flexural strength of SiC / Al / SiO2 increased with the increase of holding time, and 10 min was the best holding time.
其他文献
以Cr25Ni5Mo2Cu3RE双相不锈钢为对象,采用金相显微镜、万能拉伸试验机、冲击试验机和恒电位仪分析测试手段,研究了Mn含量对Cr25Ni5Mo2Cu3RE双相不锈钢的显微组织、力学性能及
为预测42CrMoA曲轴钢中SiO2-Al2O3-MnO系夹杂物具有良好塑性变形能力的成分控制范围,利用热力学计算软件Factsage对1873 K下42CrMoA曲轴钢钢液与SiO2-Al2O3-MnO系夹杂物间的
研究了铸态和固溶态下Mg-2.5Nd-1Cd-0.6Zr-0.4Zn镁合金的力学性能及阻尼行为。结果表明,固溶处理提高了合金抗拉强度、伸长率。室温下,铸态和固溶态合金的应变无关阻尼性能相
采用粉末冶金与原位合成相结合的技术,以铁粉、钛粉、石墨和锰铁粉等为原料,制备了碳化钛颗粒增强高锰钢复合材料。采用扫描电镜(SEM)对复合材料的微观组织进行分析。结果表
采用金相显微镜、差示扫描量热仪、扫描电镜及其能谱仪研究了Al-5.4Zn-2.0Mg-0.3Mn-0.25Cu-0.1Zr和Al-5.4Zn-2.0Mg-0.3Mn-0.35Cu-0.1Zr-0.25Sc两种合金的铸态及均匀化态显微
采用Gleeble-3500热模拟试验研究了经济型耐候钢高温塑性和连续冷却转变曲线。结果表明,试验钢塑性较好,两种试验钢的高温塑性规律基本相同,断面收缩率在40%~90%;Cu元素有扩大
概述了纳米ITO(铟锡氧化物)陶瓷粉末的制备技术。
The preparation technology of nanometer ITO (Indium Tin Oxide) ceramic powder is summarized.
进行了450、550 MPa高强耐候钢的成分设计和冶炼,通过热膨胀试验并结合金相组织,分析了该高强度耐候钢的相变规律。利用光学显微镜、扫描电镜、透射电镜以及拉伸试验对该试验
利用Gleeble-1500D热模拟试验机,对某厂A36船板钢的轧制工艺进行热模拟,通过单道次和双道次压缩试验,研究了A36钢热轧过程动态再结晶的临界应变量及静态软化行为,分析了终轧
通过MTS试验机、扫描电镜及能谱分析,对一种2100MPa级超高强度18Ni马氏体时效钢的恒应变低周疲劳破坏特性进行了研究。结果表明,时效时间对实验钢的低周应变疲劳性能的影响不