The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed.The results showed that pulse current can refine solidification grains,cut primary dentrities remarkably and reduce second dentritic arm spacing.The mechanism and effect are changed with operation parameters.
The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed. The results showed that pulse current can refine solidification grains, cut primary dentrities remarkably and reduce second dentritic arm spacing. The mechanism and effect are changed with operation parameters.