用原子参数 模式识别方法研究了AX BX2 型卤化物熔盐体系形成固溶体的规律性 ,并应用人工神经网络方法对该体系形成的最大固溶度作定量计算 ,同时预报了LiCl NiCl2 熔盐体系能形成以LiCl为基的广泛固溶体 ,其最大固溶度计算结果为 2 1 5 (mol) %NiCl2 ,与实验结果基本一致
The regularity of forming solid solution of AX BX2 halide molten salt system was studied by atomic parameter pattern recognition method. The maximum solid solubility of this system was calculated by artificial neural network method. Meanwhile, it was predicted that LiCl NiCl2 molten salt system The formation of a wide range of LiCl-based solid solution, the calculated maximum solubility of 2 1 5 (mol)% NiCl2, consistent with the experimental results