由日本株式会社研制的加压快速冷,却式真空热处理炉。是一座有效尺寸为φ1500×2000mm的立式炉,其额定温度为1350℃,常用温度为1300℃,温度均匀性为±5℃,最大处理量为3000kg。 该炉由计算机控制,具有如下特点: 1)使用冷却气体压力最大约为0.6MPa,可对钛合金等特种金属进行热处理,随着冷却能力增加,其作业时间缩短; 2)可对工件进行特殊的局部淬火; 3)可进行特种盐浴模拟试验; 4)在炉了周围设有加热装置和冷却喷嘴,所 Developed by Japan’s rapid pressure pressurized cold, but the vacuum heat treatment furnace. Is an effective size of φ1500 × 2000mm vertical furnace, the rated temperature of 1350 ℃, the common temperature of 1300 ℃, the temperature uniformity of ± 5 ℃, the maximum capacity of 3000kg. The furnace is controlled by a computer and has the following features: 1) The maximum pressure of the cooling gas is about 0.6MPa, heat treatment can be performed on special metals such as titanium alloy, and the working time is shortened as the cooling capacity increases; 2) Of the local quenching; 3) can be simulated special salt bath; 4) in the furnace with a heating device and a cooling nozzle around the