报道了一种同步辐射光束线单色仪晶体的真空安装应力形变、热缓释方法及其实验结果 ,在总功率为 2 1 0W ,最大功率密度为 1 .2 8W/mm2 时 ,晶体形变的等效曲率半径大于 2 0 0 0m ,最大隆起高度小于 0 .1 μm .
This paper reports a vacuum mounting stress deformation and thermal slow release method of a monochromator with synchrotron radiation beamline and its experimental results. When the total power is 2 1 0W and the maximum power density is 1 .28W / mm2, the crystal deformation The equivalent radius of curvature is greater than 2000m and the maximum crown height is less than 0.1μm.