The characteristic of the precipitation and growth of α2 ordered phase during aging treatment in near α Ti alloys have been investigated in terms of the influences of aging temperature, aging time and aging manner. The results exhibit that aging temperatures influence the distribution of α2 phase precipitated and cause the changes in growth speed of α2 phase. For various aging temperatures, the time to finish precipitation of α2 phase is different. The facts that various distribution characteristics and growth speed of α2 ordered phase are caused by changed aging condition imply optimal selection and control for precipitation of α2 ordered phase reachable. Some discussions on adoptable aging steps are presented.