Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature.
Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent / catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature .