Tensile properties,microstructural evolution and fracture toughness of Al 2014 alloy subjected to cryorolling followed by warm rolling (CR + WR) have been investigated in the present study.The solution-treated (ST) Al 2014 alloy is cryorolled followed by
【机 构】
：
Department of Mechanical Engineering, G.B.Pant Institute of Engineering and Technology, Pauri-Garhwa
论文部分内容阅读
Tensile properties,microstructural evolution and fracture toughness of Al 2014 alloy subjected to cryorolling followed by warm rolling (CR + WR) have been investigated in the present study.The solution-treated (ST) Al 2014 alloy is cryorolled followed by warm rolling process at different temperatures (110,170 and 210 ℃).The mechanical properties and microstructural features of deformed and undeformed Al 2014 alloys were characterised by optical microscopy,transmission electron microscopy (TEM) and scanning electron microscopy (SEM).The CR + WR samples at 170 ℃C showed an improved hardness (179 HV),tensile (UTS 499 MPa,YS 457 MPa) and fracture toughness (KQ =37.49 MPa √m,Kee =37.39 MPa vm and J integral =33.25 kJ/mm2) with respect to ST alloy as measured from the tensile and fracture toughness test.The improved mechanical properties of CR + WR alloy are attributed to grain boundary strengthening,combined recovery and recrystallisation,precipitation hardening and dynamic ageing effect during the deformation.The precipitation of metastable spherical phase Al2Cu was responsible for the improved tensile and fracture properties of finegrained Al 2014 alloy observed in the present work.
其他文献
The hot deformation behavior and workability of a new reduced activation ferritic/martensitic steel named SIMP steel for accelerator-driven system were studied.The flow curve and its microstructure were studied at 900-1200 ℃ and strain rate range of 0.001
Carbon nanofiber (CNF)-reinforced aluminum-matrix composites were fabricated via ball milling and spark plasma sintering (SPS),SPS followed by hot extrusion and powder extrusion.Two mixing conditions of CNF and aluminum powder were adopted:milling at 90 r
The corrosion behavior of stainless steel exposed to a simulated salt lake atmosphere has been investigated by analyzing the evolution of surface morphologies and corrosion products,the initiation and development of pits,and the electrochemical characteri
In this study,the effect of cooling rates on microstructures and mechanical properties in a Al-bearing hot-rolled transformation-induced plasticity steel was investigated.The experiments were carried out using hot simulation machine and hot rolling mill,w
The influence of processing temperature on grain size reduction in AA 6063 aluminum alloy subjected to repetitive corrugation and straightening (RCS) is investigated in this work.The aluminum alloy was processed by RCS at different temperatures (room temp
In this study,powder mixtures containing (Ti,W)C additions (10,20,30 and 40 wt％) were prepared and then consolidated at 1200,1250,1300 and 1350 ℃ by spark plasma sintering.The effect of (Ti,W)C additions on the microstructure and mechanical properties of
The effect of pH on the electrochemical behaviour and passive film composition of 316L stainless steel in alkaline solutions was studied using electrochemical measurements and a surface analysis method.The critical pH of 12.5 was found for the conversion
A CoCrFeMnNi high-entropy alloy with a high content of carbon was synthesized,and its hot deformation behavior was studied at the temperatures 800-1000 ℃ at the strain rates ranging from 0.001 to 0.1 s-1.As-prepared alloy is a face-centered cubic-structur
The effect of short-time aging in the temperature range between 400 and 1000 ℃ on the pitting corrosion behavior and mechanical property of a novel lean duplex stainless steel (LDSS) 2002 was investigated through the potentiostatic critical pitting temper
The influence of Fe on the microstructure and mechanical properties of P-doped Ni-Cr-Fe alloys has been investigated.Results showed that increasing Fe content refined the dendrite microstructure and enhanced the solubility of P in as-cast alloys.The chang