【摘 要】
：
研究了合金元素对Mg-12Gd-2Y-1.5Sm-0.5Zr合金显微组织和力学性能的影响。结果表明,该合金晶粒组织细小,少量Y、Sm和大量Gd固溶在镁基体里,同时有少量MgGd3、Mg24Y5和Mg41Sm5
论文部分内容阅读
研究了合金元素对Mg-12Gd-2Y-1.5Sm-0.5Zr合金显微组织和力学性能的影响。结果表明,该合金晶粒组织细小,少量Y、Sm和大量Gd固溶在镁基体里,同时有少量MgGd3、Mg24Y5和Mg41Sm5相析出;合金在室温、200、250℃下的抗拉强度分别为258、304、330 MPa;断裂为脆性断裂,与合金的低伸长率相对应。
The effects of alloying elements on the microstructure and mechanical properties of Mg-12Gd-2Y-1.5Sm-0.5Zr alloy were studied. The results show that the grain structure of the alloy is fine and a small amount of Y, Sm and a large amount of Gd are solid solution in the magnesium matrix with a small amount of MgGd3, Mg24Y5 and Mg41Sm5 phases precipitating. The tensile strengths of the alloys at room temperature and 200,250 ℃ are 258,304,330 MPa; fracture brittle fracture, and the low elongation of the alloy corresponding.
其他文献
采用高效液相色谱法对五味子药材醇提及水提部位指纹图谱进行比较研究.使用Waters SymmetryShieldTM RP18色谱柱,以乙腈-水为流动相进行梯度洗脱,建立了五味子药材醇提和水提
提出了一种基于希尔伯特-黄变换(Hilbert-Hunag transform,HHT)的电压闪变测量方法,有效实现了电网同时混有调幅波、间谐波和谐波时的闪变值计算.HHT由经验模态分解法(empiri
设计了三种材质的超声波辐射器,并通过模态分析优化设计尺寸。同时,开展铝合金超声铸造实验测试了三种辐射器对熔体的耐腐蚀性和对凝固组织的细化效果。结果表明:当Ⅰ型钛合
针对多观测样本分类问题,提出一种基于Kernel Discriminant Canonical Correlation(KDCC)来实现多观测样本分类的模型.该算法首先把原空间样本非线性的投影到高维特征空间,通
提出了有向图的SAS-全染色的概念,有向图D的SAS-全染色是D的一个正常全染色,若对D中点染色来说,不存在长为3的2色有向路.对D中弧染色来说,不存在长为4的2色有向路.并定义了有
近红外光谱数据因为样品含有相同或高度相似的基体,往往具有相似的光谱形状,而某些光谱可能只是反映了基体信息,而与被测物含量没有相关性,称之为无信息光谱。因为光谱的高相
采用微波辐射加热法,从巴豆醛出发,在乙醇中制备巴豆醛肟,进一步脱水生成标题化合物,并考察了微波输出功率、反应时间、乙酸酐的用量对反应的影响。最优的反应条件为:微波输
以内酰胺与硫酸二甲酯为原料合成中间体环状亚胺醚,再与磺酰胺的进一步缩合反应合成出标题化合物。利用1HNMR,13CNMR和高分辨质谱(HRMS)等方法确证了标题化合物的结构。
The
在自反、严格凸、具有(K)性质光滑Banach空间中,提出了一种杂交投影迭代算法,并证明了该算法强收敛到其公共不动点,改进并推广了Zhou的相关工作.
目的 比较急诊抢救室脓毒症、全身炎症反应综合征(systemic inflammatory response syndrome.SIRS)与非SIRS患者尿微量白蛋白与尿肌酐之比(albumin/creatinine ratio,ACR)阳