The tensile equipment of the advanced confocal scanning laser microscope(CSLM)was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting.The results show that,at the strain rate of 0.0005 s~(-1),the strip clearly shows signs of brittleness at around 600℃and its plasticity falls considerably between 750℃and 600℃.This is because during the transformation from austenite to ferrite,the low strength ferrite at the austenite grain boundaries greatly reduces the steel’s high temperature plasticity.The subsequent strip coiling process should be controlled at less than the brittle temperature of approximately 600℃,so cracks at the coiling stage can be prevented.
The tensile equipment of the advanced confocal scanning laser microscope (CSLM) was used to research the high temperature mechanical properties of low carbon silicon-bearing steel by twin-roll strip casting.The results show that at the strain rate of 0.0005 s ~ ( -1), the strip clearly shows signs of brittleness at around 600 ° C and its plasticity falls urge between 750 ° C and 600 ° C. This is because during the transformation from austenite to ferrite, the low strength ferrite at the austenite grain boundaries greatly reduces the steel’s high temperature plasticity. The subsequent strip coiling process should be controlled at less than the brittle temperature of approximately 600 ℃, so cracks at the coiling stage can be prevented.