The properties of high entropy alloys (HEAs) depend on their phase structures and compositions.How-ever,it is difficult to control the composition of the HEAs that contain highly volatile metals by the conventional arc melting method.In this paper,homogeneous powdery face centered cubic (FCC) phase Fe0.5CoNiCuZnx HEAs were prepared by the electrolysis of metal oxides in molten Na2CO3-K2CO3 using a stable Ni11Fe10Cu inert oxygen-evolution anode.The use of oxide precursors and relatively low synthetic temperature are beneficial to efficiently preparing HEAs that contain highly volatile elements such as Zn.Moreover,the microstructures and compositions of the electrolytic HEAs can be easily tailored by adjust-ing the components of oxide precursors,then further regulating its properties.Thus,the electrocatalytic activity of Fe0.5CoNiCuZnx HEAs towards oxygen evolution reactions (OER) was investigated in 1 M KOH.The results show that Zn promotes the OER activity of Fe0.5CoNiCuZnx HEAs,i.e.,the HEA(Zn0.8) shows the best OER activity exhibiting a low overpotential of 340 mV at 10 mA/cm2 and excellent stability of 24 h.Hence,molten salt electrolysis not only provides a green approach to prepare Fe0.sCoNiCuZnx HEAs but also offers an effective way to regulate the structure of the alloys and thereby optimizes the electro-catalytic activities for water electrolysis.