【摘 要】
：
研究了不同焊接电流下,堆焊SAF2304双相不锈钢钢筋焊缝显微组织及显微硬度的变化。结果表明,焊接电流由100 A增大到130 A,双相不锈钢热影响区奥氏体含量由24.4%增大到33.6%,
论文部分内容阅读
研究了不同焊接电流下,堆焊SAF2304双相不锈钢钢筋焊缝显微组织及显微硬度的变化。结果表明,焊接电流由100 A增大到130 A,双相不锈钢热影响区奥氏体含量由24.4%增大到33.6%,显微硬度降低4 HV,焊缝区二次相析出数量增多,显微硬度降低10 HV。焊后双相不锈钢钢筋热影响区出现软化现象,但对钢筋性能影响不明显。
The microstructure and microhardness of SAF2304 duplex stainless steel welded joints with different welding current were studied. The results show that the welding current increases from 100 A to 130 A, the austenite content in the HAZ increases from 24.4% to 33.6%, the microhardness decreases 4 HV, and the amount of secondary phase precipitates increases in the weld zone. The microhardness is reduced by 10 HV. After welding, the heat-affected zone of duplex stainless steel rebar appears softening phenomenon, but the effect on reinforcing steel performance is not obvious.
其他文献
目的:探讨剖宫产产后出血中子宫背带式缝合术治疗的临床效果.方法:选择我院2008年1月至2011年1月收治的剖宫产产后出血患者84例,随机分为两组,对照组40例采取传统止血治疗,观
目的:探讨人文护理在普外科手术患者康复过程中的重要作用.方法:在患者住院过程中,注重人文护理,营造人文氛围,将人性化服务落实到手术前后护理的整个过程.结果:医院对护士实
今年是南京艺术学院学报创刊七十周年(1918—1978—1988),复刊十周年。七十年来由于政治风云变幻对学术研究事业的影响,南京艺术学院学报《美术》、《葱岭》、《艺术旬刊》
目的 探讨胸部创伤的诊断与治疗.方法 根据胸部创伤的位置及临床表现,利用放射线、CT、超声、胸腔穿刺或腹腔穿刺等检查方法及时发现胸腔内脏器的损伤情况,根据不同情况行单
目的:探究老年慢性支气管炎的有效治疗方法.方法:对我院80例老年慢支患者的临床资料进行回顾性分析.结果:经综合性治疗后,80例中有35例治愈,30例显效,13例见效,2例无效,总有
【摘要】本文针对应用型本科学生数学应用意识的淡薄，以及对数学的重视不够的原因和后果进行分析，并对如何培养学生在学习高等数学课程的应用意识方面提出一些建议。 【关键词】应用型本科 高等数学 数学应用意识 【中图分类号】G642.4 【文献标识码】A 【文章编号】2095-3089（2014）10 -0006-02 高等数学是应用型本科院校中经管类及财经类专业必修的基础课程之一，熟练的掌握并应用
笔者根据培养创造力的原理,结合家庭教育、学校教育,从培养良好个性、提供自由宽松环境等方面入手,对某小学四年级学生进行了小学生创造力培养的试验研究.结果发现,实验班级
高血压是老年人最常见的疾病之一,老年高血压的本身特点就决定了其有较高的致死、致残率,对老年人的健康危害较大.根据患者自身疾病特点采用最适宜的降压药物,通过积极有效的
目的:探讨高血压脑出血微创穿刺引流时机及疗效分析.方法:回顾性分析对我科从2007年1月至2010年12月收治的78例高血压脑出血患者用YL-I型穿刺针行微创血肿穿刺引流,其中18例