18Mn18Cr0.5N steel with an initial grain size of 28–177μm was processed by 2.5%–20%cold rolling and annealing at 1000°C for 24 h,and the grain boundary character distribution was examined via electron backscatter diffraction.Low strain(2.5%)favored t