【摘 要】
:
A new solvent extraction system of Au(Ⅰ)by surfactant CTMAB-TBP-inert diluent-Au(CN)2--H2O was investigated and established.The infrared spectra and the conduc
【机 构】
:
Institute of Precious Metals,College of Chemistry and Molecular Engineering
论文部分内容阅读
A new solvent extraction system of Au(Ⅰ)by surfactant CTMAB-TBP-inert diluent-Au(CN)2--H2O was investigated and established.The infrared spectra and the conductivities of loaded organic phases containing Au(Ⅰ)were recorded stage by stage.It was reported that in the presence of salting-out agents the pencent extraction of Au(Ⅰ)decreased,and the conversion of emulsions from W/O to O/W happened in the extraction processed.The results demonstrate that the extraction process of Au(CN)2-is carried out by two steps.First,an associated molecule between CTMA+ and TBP,as (C16 H33) (CH3)3 N+·H2O·O= P(OC4 H9)3,is formed by dint of water molecule,then it will pull Au(CN)2-into the organic phase based on the electro-neutrality.
其他文献
To investigate the biomineralization behavior of silk fibroin and to valuate the biodegradation and biocompatibility of the hybrid biomaterial, the calcium phos
本文介绍了在定期检验中发现二氧化碳贮罐罐顶压力表接管腐蚀膨胀,对该腐蚀的现状和产生的原因及危害性做了分析,提出了今后的防范措施,以避免小接管引发大事故。
Bone-like hydroxyapatite( HAp ) powders were synthesized using a reverse microemulsion method without further calcine processing. Synthesis conditions had signi
An experimental investigation was conducted to identify the characteristics of crack growth in high performance concrete (HPC) subjected to fire, including two
The horizontal direct chill (HDC) casting process is a well-established production route for aluminum alloy ingot but the ingot may suffer from macrosegregation
The particle size has a strong impact on the interactions between nanoparticles and cells. However, the synthesis process of nanoparticles limits the range of a
The paper presents a framework for developing a variety of video transition effects. The framework is designed to deal with the problem of inefficiency for prog
CoFe2O4 nanoparticles that were synthesized by coprecipitation method were heat-treated at different temperature, and analyzed by XRD and TEM. The particle size
A series of experiments were carried out using different admixed lubricant contents,different compaction pressures and temperatures in order to study the warm c
Diamond-like carbon ( DLC ) -films were successfully deposited on Ti- 50.8at% Ni using plasma based ion implantation (PBII) technique. The influence of the puls