【摘 要】
:
The aging behavior of single lap joints (SLJ) in hygrothermal cycles was investigated and compared by using a shearing strength test, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TG/DTG), energy dispersive spectrometry (EDS)
【机 构】
:
School of Mechanical Engineering, North China University of Water Resources and Electric Power, Zhen
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
The aging behavior of single lap joints (SLJ) in hygrothermal cycles was investigated and compared by using a shearing strength test, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TG/DTG), energy dispersive spectrometry (EDS) and scanning electronic microscopy (SEM). The temperature/relative humidity was set at 80 ℃/95% and –40 ℃/30% for 20 cycles, 40 cycles, and 60 cycles (one cycle was 12 hours), respectively. The experimental results show that hygrothermal aging significantly decreases the failure strength of adhesive joints. However, the failure displacement increases as the number of aging cycles increases. In addition, hygrothermal aging changes the failure mode of the adhesive joints from a cohesive fracture in un-aged adhesive layers to an interfacial failure of aged adhesive joints.
其他文献
The effects of aging time and temperature on the formation and growth behavior of interfacial intermetallic compound (IMC) of Sn-16Sb/Cu(wt%) solder joints prepared by using dip soldering were investigated. The results show that the major IMCs between Sn-
Titania (TiO2) nanorod powder was prepared by nonhydrolytic sol-gel method using titanic chloride (TiCl4) as titanium source, methylene dichloride (CH2Cl2) as solvent, absolute ethyl alcohol (CH-3CH2OH) as oxygen donor. The effects of Si4+ doping on the T
Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi3+ and Ce 4+ containing aqueous solution.Techniques of X-ray diffraction(XRD),transmission electron microscopic(TEM)and Fourier transform infrared spectroscopy(F
A fixed-point observation method was designed to research the dynamic tribologieal performance of one certain resin-based friction materials.The friction test was performed through a constant speed friction tester under various temperature conditions.It w
Polydimethylsiloxane (PDMS)-polystyrene (PS) interpenetrating polymer network (IPN) was prepared and characterized by FTIR, TGA, WCA, swelling experiments, and SEM. The IPN was used for pervaporation (PV) recovery of butanol. Both the permeation flux and
The effects of the annealing process on the mechanical properties and crystallization behaviors of polypropylene random copolymer (PP-R) composites were investigated using differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and d
To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensi
The use of the thermal power plant ashes including fly ash (FA) and bottom ash (BA) for producing unfired building bricks (UBB) using sodium hydroxide (NaOH) solution as an alkaline activator was investigated. A low applied forming pressure of 0.5 MPa and
The effect of homogenization treatment on the corrosion behavior and corrosion mechanism of Mg-Y alloys in 3.5 wt% NaCl solution was investigated by electrochemical characterization, immersion testing and SEM observations. The diffusion kinetics model of
To decrease the modulus and increase the mechanical properties of recycled PET by introducing the flexible segments, the recycled polyethylene-terephthalate (PET) was modified by the chain extender produced with 2, 4, 6, 8-tetramethyl-2, 4, 6, 8-tetra (2,