钛的质量分数低于0.10%时,显示石墨化作用;超过0.10%时则显示出稳定碳化物作用。利用钛的“双重性”,加入适当的质量分数,是提高铸铁材料质量的重要课题之一。
When the mass fraction of titanium is less than 0.10%, graphitization is shown, while when it exceeds 0.10%, it shows a stable carbidation. The use of titanium’s “duality”, adding the appropriate mass fraction, is one of the important issues to improve the quality of cast iron materials.