【摘 要】
：
Inadequate strength at the bone/cement interface is one of the main drawbacks of poly(methylmethacrylate) (PMMA) bone cement in the current orthopedic surgeries.In the present work,a partially degradable PMMA/Mg composite bone cement (PMC) was developed f
【机 构】
：
Orthopaedic Institute, Soochow University, Suzhou 215006,China;Department of Orthopaedics, The First
论文部分内容阅读
Inadequate strength at the bone/cement interface is one of the main drawbacks of poly(methylmethacrylate) (PMMA) bone cement in the current orthopedic surgeries.In the present work,a partially degradable PMMA/Mg composite bone cement (PMC) was developed for enhancing the bone/cement interfacial strength,which is proposed to be accomplished by increasing the osteo-conductivity of PMMA and enhancing the mechanicai interlocking between bone tissue and the porous PMMA surface formed by the degradation of Mg on the surface of the cement.PMCs were prepared with various concentrations of Mg particles with different sizes and alloy compositions.The effects of Mg particle size,composition and content on the injectability,mechanical and degradation properties,and biocompatibility of PMCs were evaluated.The results show that these parameters affected the properties of the PMCs simultaneously.The good injectability and compressive strengths of PMMA were preserved,while the compatibility to osteoblasts was enhanced when adding Mg particles in a proper manner.The PMCs degraded at the surface with time and formed porous surface structures in the physiological environment,while maintaining the original compressive strengths.This preliminary study shows that the PMC is promising for minimally invasive orthopedic surgery;however,it still requires to be optimized and evaluated in the future.
其他文献
The work is mainly to study the thermal stability including the phase stability,microstructure and tribo-mechanical properties of the A1B2-type WB2 and W-B-N (5.6 at.％ N) films annealed in vacuum at various temperatures,which are deposited on Si and GY8 s
The dynamic mechanical relaxation behavior of Ti36.2Zr30.3Cu8.3Fe4Be21.2 bulk metallic glass with good glass-forming ability was investigated by mechanical spectroscopy.The mechanical relaxation behavior was analyzed in the framework of quasi-point defect
CoFe2O4 nanoparticles (NPs) and surface modified with gold (Au) have been synthesized by a thermal decomposition method.The obtained NPs and formation of CoFe2O4@Au core-shell (CS) were confirmed by characterizing their structural and optical properties u
Plasma nitriding is a widely used technology to enhance the surface performance and extend the service life of alloy parts.The current research mainly focuses on the influences of time,temperature,gas type and pressure parameters on nitriding behavior,whi
This paper clarifies two issues related to the prior cathodic polarisation treatment (PCPT) for the potentiodynamic polarisation test: whether PCPT can (1) remove the air-formed surface film and (2) affect the polarisation test results.X-ray photoelectron
A new method for evaluating the compactness of rust layers on steels has been proposed in the present study.The method includes adsorption and dehydration process of anhydrous ethanol.The protective ability of rust layers can be qualitatively reflected by
Electron diffraction was used to study the local atomic structure of Cu49Hf42Al9 metallic glasses (MGs).The amorphous nature of the MG was fully retained after the compression test.The partial radial distribution functions (PRDFs) of the MG structure obta
The effect of grain size on the mechanical properties of a high-manganese (Mn) austenitic steel was investigated via electron-backscattered diffraction,transmission electron microscope,X-ray diffraction,and tensile and impact tests at 25 ℃ and-196 ℃.The H
Sandwich-like Al/Ti/Al-laminated composites have many advantages such as low density and high specific strength with value in mechanical manufacturing and aerospace engineering.Here,Al/Ti/Al-laminated composites were fabricated by hot roll bonding and sub