【摘 要】
:
采用XRD、DSC、VSM等分析检测方法,研究了Fe73.5Cu1Nb3Si13.5B9软磁材料的最佳退火工艺。结果表明:合金经550℃×1h退火后可获得由纳米晶α-Fe(Si)相和少量非晶相所组成的复
【机 构】
:
山东科技大学材料科学与工程学院,莱钢集团机械制造有限公司,
论文部分内容阅读
采用XRD、DSC、VSM等分析检测方法,研究了Fe73.5Cu1Nb3Si13.5B9软磁材料的最佳退火工艺。结果表明:合金经550℃×1h退火后可获得由纳米晶α-Fe(Si)相和少量非晶相所组成的复相组织,具有优异的综合软磁性能。随退火温度的升高,α-Fe(Si)软磁相晶粒尺寸逐渐增加,Fe2B硬磁相不断析出,从而导致合金的软磁性能下降。
The optimum annealing process of Fe73.5Cu1Nb3Si13.5B9 soft magnetic materials was studied by XRD, DSC and VSM. The results show that the complex phase composed of nanocrystalline α-Fe (Si) phase and a small amount of amorphous phase can be obtained by annealing at 550 ℃ for 1h, which has excellent comprehensive soft magnetic properties. With the increase of annealing temperature, the grain size of α-Fe (Si) soft magnetic phase gradually increases, and the Fe2B hard magnetic phase is continuously precipitated, resulting in the decrease of the soft magnetic properties of the alloy.
其他文献
目的:评价和分析综合干预对域类切口手术围手术期抗菌药物预防性应用的影响,以促进域类切口手术围手术期合理使用抗菌药物。方法:通过行政管理与药学干预相结合的方法,对对照组(20
采用自配的合金粉末,对45钢进行激光熔覆处理。利用OM、XRD和显微硬度计对熔覆层的组织结构及硬度进行了研究。结果表明,B最佳含量为1.5%;熔覆层基体相为α-Fe,基体相上分布
文章针对分形编码算法编码时间太长等缺点提出了对编码图象进行差分和分级逼近的新的分形编码算法.对这一思想的可行性在理论上进行了有益的探索,给出了该算法成立的理论基础
采用热喷涂+激光重熔工艺,在Q235低碳钢板上制备了Ni60涂层,对涂层微观组织、硬度分布规律进行了分析。结果表明:涂层经过激光重熔后,外观质量良好,无裂纹缺陷,其组织组成物
《西游记》文中包含有中医哲学思维,阴阳、五行等中医思想.文中载有两篇药名体诗以及多味中药的药性和对应治疗的症状;描述了多种疾病的病名、相关疾病的诊断、治疗以及中医
利用微弧氧化和化学镀镍在AZ91D镁合金表面制备了复合涂层,采用动电位极化曲线测试和电化学阻抗测试等方法研究微弧氧化和化学镀镍复合涂层在3.5%NaCl溶液中的腐蚀行为。结果
将Al、Si配比为1:1、11:9、3:2(at%)的料浆分别涂刷在带有碳化硅内涂层的碳/碳复合材料表面,分别在1400、1450、1500℃进行扩散处理制得Al-Si合金外涂层。另外,在1500℃静态
目的:观察软肝散对慢性乙型肝炎肝纤维化的临床疗效.方法:64例慢性乙型肝炎患者随机分治疗组和对照组,治疗组给予恩替卡韦联合软肝散口服,对照组给予恩替卡韦口服,疗程48周,
研究了采用氧-乙炔火焰粉末喷熔工艺修复磨损超差的40CrNiMoA合金调质钢制零部件的方法,提出了40CrNiMoA合金调质钢件的喷熔修复工艺。
The method of oxygen-acetylene fla
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥