Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique. The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures. The thermal parameter (B) of Sm is larger than that of Sb, Fe, and Co, indicating that Sm “rattled” in Sb-icosahedron voids. The effects of filling atom Sm on thermoelectric properties of these compounds were investigated. With the increase of Sm filling fraction (y), electrical conductivity decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0.32. At 750 K, the highest figure of merit of 0.68 was obtained for Sm0.32Fe1.47Co2.53Sb12.
The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures. The thermal parameter (B) of Sm is larger than that that of Sb, Fe, and Co, indicating that Sm “rattled ” in Sb-icosahedron voids. The effects of filling atom Sm on thermoelectric properties of these compounds were investigated. With the increase of Sm filling fraction (y) decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0.32. At 750 K, the highest figure of merit of 0.68 was obtained as Sm0.32Fe1.47Co2.53Sb12.