For 308L and 347L weld metals of austenitc stainless steels (ASS), hydrogen induced cracking (HIC) occurred during dynamically charging under constant load. The
The bonding of steel plate to aluminum liquid was conducted using rapid solidification.The influence of diffusion time on interfacial structure was studied.The