Au nanostructures were prepared on uniform Cu2O octahedra and rhombic dodecahedra via the galvanic replacement reaction between HAuCl4 and Cu2O.The compositions and structures were studied by Scanning Electron Microscope (SEM),Transmission Electron Micros
【机 构】
：
Hefei National Laboratory for Physical Sciences at the Microscale,CAS Key Laboratory of Materials fo
论文部分内容阅读
Au nanostructures were prepared on uniform Cu2O octahedra and rhombic dodecahedra via the galvanic replacement reaction between HAuCl4 and Cu2O.The compositions and structures were studied by Scanning Electron Microscope (SEM),Transmission Electron Microscope (TEM),High-Resolution Transmission Electron Microscope (HRTEM),X-Ray Diffraction (XRD),X-Ray Absorption Spectroscopy (XAS),X-ray Photoelectron Spectroscopy (XPS) and in-situ DRIFTS spectroscopy of CO adsorption.Different from the formation of Au-Cu alloys on Cu2O cubes by the galvanic replacement reaction (ChemNanoMat 2 (2016) 861-865),metallic Au particles and positively-charged Au clusters form on Cu2O octahedra and rhombic dodecahedra at very small Au loadings and only metallic Au particles form at large Au loadings.Metallic Au particles on Cu2O octahedra and rhombic dodecahedra are more active in catalyzing the liquid phase aerobic oxidation reaction of benzyl alcohol than positively-charged Au clusters.These results demonstrate an obvious morphology effect of Cu2O nanocrystals on the liquid-solid interfacial reactions and prove oxide morphology as an effective strategy to tune the surface reactivity and catalytic performance.
其他文献
The demand of microelectronic devices postulated high energetic flexible energy storage devices.Flexible solid state supercapacitor is flawless possible candidate to fulfill the requirement of microelectronic devices.This investigation provides practical
Preparation of high-quality films plays an important role to achieve high-performance nonfullerene (NF) organic solar cells.NF active layer films are typically fabricated by spin coating.Novel fabrication methods to process the NF active layer are desirab
A homogeneous better-dispersed ultrathin nanosheets (ca.5 nm) of cobalt-nickel layered double hydroxides (LDH) supported on nickel foam scaffold was synthesized using controllable electrodeposition approach for high efficiency electrode materials of new s
For some specific catalytic reaction,how to construct active sites on two dimensional materials is of great scientific significance.Dye-sensitized solar cells (DSCs) can be viewed as one representative photovoltaics because in which liquid electrolyte wit
Aqueous Zn//MnO2 batteries are emerging as promising large-scale energy storage devices owing m their cost-effectiveness,high safety,high output voltage,and energy density.However,the MnO2 cathode suffers from intrinsically poor rate performance and rapid
Methanol to gasoline reaction was investigated on two prepared ZSM-5 catalysts.The first one was a conventional catalyst denoted as ZSM-5(C) and the other was a hierarchical catalyst-ZSM-5(S) which was prepared by incorporation of table sugar in catalyst
Poly(amide-6-b-ethylene oxide) (Pebax1657)/1-butyl-3-methylimidazo-lium bis[trifluoromethyl)sulfonyl]-imide ([Bmim][Tf2N]) blend membranes with different [Bmim][Tf2N] contents were prepared via solution casting and solvent evaporation method,The permeatio
Hydrodeoxygenation (HDO) is an effective alternative to produce value-added chemicals and liquid fuels by removing oxygen from lignin-derived compounds.Sulfide catalysts have been proved to have good activity for the HDO and particularly high selectivity