The corrosion behavior of the nitinol alloy was studied in various corrosion media of different Cl–ion concentrations. The results demonstrate that the Cl–ion
Low speed impact damage in thermosetting composites due to a 12.7mm diameter impactor is more severe than delaminations, flawed holes and porosity[1,2]. The most