Friction stir welding(FSW) of high strength aluminum alloys has been emerged as an alternative joining technique to avoid the problems during fusion welding.In recent times FSW is being used for armor grade AA7075 aluminum alloy in defense,aerospace and marine applications where it has to serve in non uniform loading and corrosive environments.Even though friction stir welds of AA7075 alloy possess better mechanical properties but suffer from poor corrosion resistance.The present work involves use of retrogression and reaging(RRA) post weld heat treatment to improve the corrosion resistance of welded joints of aluminum alloys.An attempt also has been made to change the chemical composition of the weld nugget by adding B4C nano particles with the aid of the FSW on a specially prepared base metal plate in butt position.The effects of peak aged condition(T6),RRA and addition of B4C nano particles on microstructure,hardness and pitting corrosion of nugget zone of the friction stir welds of AA7075 alloy have been studied.Even though RRA improved the pitting corrosion resistance,its hardness was slightly lost.Significant improvement in pitting corrosion resistance was achieved with addition of boron carbide powder and post weld heat treatment of RRA. Friction stir welding (FSW) of high strength aluminum alloys has been emerged as an alternative joining technique to avoid the problems during fusion welding. Recent times FSW is being used for armor grade AA7075 aluminum alloy in defense, aerospace and marine applications where it has to serve in non uniform loading and corrosive environments. Even though the friction stir welds of AA7075 alloy possess better mechanical properties but suffer from poor corrosion resistance. the present work involves use of retrogression and reaging (RRA) post weld heat treatment to improve the corrosion resistance of welded joints of aluminum alloys. An attempt also has been made to change the chemical composition of the weld nugget by adding B4C nano particles with the aid of the FSW on specially prepared base metal plate in butt position. (T6), RRA and addition of B4C nano particles on microstructure, hardness and pitting corrosion of nugget zone of the friction stir welds of AA7075 alloy have been studied. Although though RRA improved the pitting corrosion resistance, its hardness was slightly lost. Significant improvement in pitting corrosion resistance was achieved with addition of boron carbide powder and post weld heat treatment of RRA.