In this paper, the microstructure evolution of the rapidly solidified (RS) Mg61.7Zn34Gd4.3 (at%, atomic ratio) alloy at high temperatures was investigated. The hardness and elastic modulus of the main precipitated phases were also analyzed and compared wi