【摘 要】
：
In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the c
【机 构】
：
College of Textiles, Donghua University,Shanghai 201620, China;Key Laboratory of Textile Science and
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the cotton fibers were pre-treated by hydrogen peroxide solution(H2O2) and sodium hydroxide(NaOH), urea(CON2H4). Secondly, the fabric was fabricated via in situ deposition. The effects of concentration of treatment liquid, ammonia-smoking time and curing temperature on the tensile property of the fabric, UV blocking property and water-washing durability test of as-obtained cotton fabrics were investigated. Thirdly, the as-obtained cotton sample was characterized by X-ray diffraction(XRD) and field emission scanning electron microscopy(FESEM). It was shown that ZnO nanoparticles were assembled between cotton fibers, the surface and inside of the lumen and the mesopores of cotton fibers, while the content of nano-ZnO assembled in fabric can reach 15.63wt％. It is proved that the finished fabric can obtain a very excellent UV blocking property, under the condition of zinc ion in concentration of 15wt％, ammonia-smoking time for 10 min, curing temperature at 150 ℃ for 2 min.
其他文献
The surface of gadolinium was covered with a layer of Al film(10-15 μm) by hot-press.Corrosion resistance,thermal conductivity and diffusivity of the composites were studied.As a result,temperature and pressure are the main factors that influence the comb
Atri-polyphosphate was used as a corrosion inhibitor in the seawater prepared coral concrete,and its influence on the corrosion behavior of carbon steel,304 austenitic stainless steel,and 2205 duplex stainless steel was studied by the open-circuit potenti
In the absence of commonly used seed layer, we can still successfully synthesized aligned ZnO nanowire arrays by the hydrothermal method. By using aluminum-doped zinc oxide (AZO) glass as a substrate, high-density and vertically aligned ZnO nanowires were
LDHs was introduced into 70# asphalt binder by different weight ratio. Asphalt penetration test, soft point test, ductility test, viscosity test, dynamic shear rheometer (DSR) test and Fourier transform infrared (FTIR) test, were conducted to characterize
Slag glass melting is usually performed on a laboratory scale in crucibles, which are economically viable tools for the production of slag glass-ceramics. In this work, quaternary CaO-Al2O3-MgO-SiO2 (CAMS) glass-ceramics were prepared by melting the taili
The microstructural evolution of C-(A)-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt％ Na2SO4 solution for different ages was comparatively investigated, by means of 29Si NMR spectroscopy, and SEM-EDS analysis. Additionally, molecular
Ferroelectric and leakage properties are important for ferroelectric applications. Pure and Nd-doped (x=0.05-0.20) BiFeO3 thin films were fabricated by sol-gel method on FTO substrates. The phase structure, surface morphology, leakage current, ferroelectr
Amphiphilic CS-SA polymers were prepared using the SA modified by small molecule water-soluble chitosan, and CS-SA nanomicelles and FF/CS-SA nanomicelles were prepared by using CSSA polymers as the material with dialysis-ultrasound method. CS-SA polymers,
A modified Bridgman directional solidification technique was used to prepare Fe-Al-Ta eutectic in situ composites at different growth rates ranging from 6 to 80 μm/s. The directionally solidified Fe-Al-Ta eutectic composites are composed of two phases: Fe
Early hydration mechanism of cement-based materials with silica fume, nano-SiO2 and silica sol of different contents was investigated, and the detailed effect of these Si-rich mineral admixtures in three stages of early hydration (NG, I, D) using kinetics