对S355NL连铸圆坯表面横裂纹形成原因进行了低倍和高倍凝固组织研究,并对裂纹区域微观凝固组织进行了能谱成分分析,根据分析结果推测:表面横裂纹萌生于结晶器,出结晶器后在二
【机 构】
：
山西太钢不锈钢股份有限公司技术中心,太原理工大学材料科学与工程学院,
论文部分内容阅读
对S355NL连铸圆坯表面横裂纹形成原因进行了低倍和高倍凝固组织研究,并对裂纹区域微观凝固组织进行了能谱成分分析,根据分析结果推测:表面横裂纹萌生于结晶器,出结晶器后在二冷区扩展,进入矫直阶段裂纹沿着振痕波谷处发生了撕裂和贯通。实践表明,通过采取提高拉速8.69%、降低二次冷却水强度10%和采用包晶钢专用保护渣的措施可预防包晶钢表面横向裂纹的发生。
According to the analysis results, it is inferred that the surface transverse cracks originated in the crystallizer and crystallized out, and the microstructure of microstructure of the microstructure in the cracked area was analyzed. After the expansion in the second cold zone, into the straightening stage crack along the vibration mark trough occurred at the tear and through. Practice shows that by increasing the pulling rate of 8.69%, reducing the secondary cooling water strength of 10% and the use of special protective measures of peritectic steel can prevent the occurrence of transverse cracks on the surface of peritectic steel.
其他文献
针对320 mm×410 mm断面生产重轨钢宏观偏析较大的问题,在分析该断面生产重轨钢宏观偏析控制工艺难点的基础上,开展了电磁搅拌电流强度对比试验、重压下压下总量对比试验以及
能否合作共事可不是一件小事,因为我们将会在一起长时间合作。在后来的8个月中,我和张去了5次中国,最短的那次也有3个星期。我们要做的事情很多。在北京建立一个合法的公司
通过建立顶燃式热风炉炉壳弹塑性模型,研究了盲板力作用下热风炉炉壳的受力状态及变形情况.结果表明,在内部气体压力作用下,热风炉炉壳及热风总管变形弯曲挤压热风支管,导致
湖南会同若水乡檀木湾村有一株远近闻名的千年古樟树,它紧靠沅水上游的巫水河畔,它左右前三面有巫水环绕,背靠大片村庄。树干胸围13.1米,树高37米左右,冠幅962平方米,枝叶繁
前不久,广东一公交司机因不满休假期间被要求顶班而飙车泄愤,导致4人死亡。这种野蛮而疯狂行为应当受到法律的严惩。但是,在震惊的同时,我们还应充分的反思,以期亡羊补牢,防
夏日的晚风温暖而多情,静静地写在你的脸上,刻在我的心里。 默默的是你的表情,期待的是我的眼眸,第一次把你从虚拟的世界中牵了出来。原以为,那只是一场游戏一场梦,然而,当
球团矿的固结方式主要是赤铁矿的固相固结,即通过赤铁矿的再结晶互相连接,使球团具有一定的强度。为了研究赤铁矿形态对球团强度的影响,将球团矿内的赤铁矿按形态分为:大颗粒
近年来，党中央、国务院十分关心农村留守儿童的健康成长，河南省委、省政府高度重视农村留守儿童工作。这也是本刊关注的焦点之一。 所谓农村留守儿童，是指那些父母外出打工后，被遗留在家乡的农村儿童，他们或独自生活，或被托付给祖辈、亲戚抚养。 据有关部门统计，目前全国农村留守儿童人数已达5800万，作为第一劳务输出大省的河南，农村留守儿童在255万左右。 农村留守儿童正处于成长发育阶段，由于缺乏亲情、
我是医生…… 有一年医学院的学生去某精神病院见习,初次进入这一“特殊领域”,学生有几分紧张和几分莫名的兴奋。 一群人簇拥着带教老师进了大门,又进了病房,病房的铁门“
在文书立卷工作中,不论采取何种立卷方法,都必须准确地确定每一份归档文件材料的“问题”,因为“问题特征”是文件材料最主要的特征。在确定文件材料组卷时,要求一个立档单