论文部分内容阅读
Dislocation internal friction,elastic modulusdefect and their ratio r have been studied in an-nealed and plastically deformed Zn single crystals inthe temperature range of 80 to 300 K in a widerange of oscillation amplitudes.The results ob-tained are disc