【摘 要】
：
研究OCr17Ni7A1沉淀硬化不锈钢经不同热处理制度处理后对性能的影响得出,热处理最高固溶温度不应超过1100℃,热加工温度宜低于1150℃;奥氏体化处理温度的提高将使奥氏体稳定
论文部分内容阅读
研究OCr17Ni7A1沉淀硬化不锈钢经不同热处理制度处理后对性能的影响得出,热处理最高固溶温度不应超过1100℃,热加工温度宜低于1150℃;奥氏体化处理温度的提高将使奥氏体稳定化的倾向加重,室温停留时间对最终性能的影响也随之增大,不同热处理制度在时效温度560℃以上时其性能趋向一致。
The effect of different treatment systems on the properties of OCr17Ni7A1 precipitation-hardened stainless steel was studied. The maximum solution temperature for heat treatment should not exceed 1100 ℃ and the heat treatment temperature should be lower than 1150 ℃. The increase of austenitizing temperature will make austenite The tendency of the body to stabilize is aggravated, the influence of the residence time at room temperature on the final performance also increases, and the performance of different heat treatment systems tends to be consistent when the aging temperature is above 560 ° C.
其他文献
我们有一台南通机床厂生产的J320-1型三坐标立式数控铣床,使用一段时间后,工作台出现沿X轴向的抖动现象,同时,X轴伺服电机还带有异常噪音。这种现象的出现是无规律的,一般随
据新闻媒体报道,1998年10月1日,正当人们沉浸在国庆佳节的欢乐之中时,暂住在哈尔滨市的打工仔王景波却残忍地把妻子砍死在床上,原因是性冷淡的妻子拒绝和他同房。今年27岁的
齿轮在渗碳过程中,不可避免地产生形状和尺寸的变化。我们总结和探讨了齿轮结构特点与变形的规律,以稳定和控制齿轮的变形,提高其尺寸精度和使用寿命。一、减少和控制齿轮变
在塑料薄膜表面高速连续真空镀铝研究和扩大生产应用取得系统的研究结果的基础上［１、２］，针对我国包装装璜用真空镀铝纸工业发展中遇到的问题，进行了调查研究和国内外考察，对真空镀铝
7、关于企业价值评估中所采用方法的调查(1)是否采用了多种评估方法对同一企业进行评估除27份问卷未选择答案之外,有效样本为887个。其中,采用过多种评估方法对同一企业进行
一、前言在船体建造过程中,有许多焊接接头因受到各种条件的限制,不能把工件翻转,所以只能用仰位置的碳弧气刨和手工
I. Foreword During the construction of the hull, t
厦门市瑞景小学坐落于美丽的鹭岛云顶山之下,自学校创办以来,本着“一切为了孩子,为了孩子的一切”的办学思想,沿着“规范、高效、优质、特色”
Xiamen Ruijing primary sch
本文介绍了紫外光固化润滑涂料主要组分(基料、光敏剂、润滑性添加剂以及活性稀释剂等)的主要品种、性能和发展,还介绍了典型的紫外光固化润滑涂料的配方,並概括了光固化涂层
一年前的此时,还很少有战锤玩家想到中国可以举办金恶魔涂装比赛,但是2009年11月,北京概念之舟科技有限着责任公司及各地的战锤俱乐部揭开了中国“金恶魔”大赛的序幕,来自全
摘自冶金部钢铁研究总院研究生孙政的硕士学位论文,导师:陈良材、韩怀月 00Cr25Ni20Nb不锈钢是为原子能后处理工程研制的钢种。这种钢在以硝酸为主的混酸介质中具有优良的耐