【摘 要】
：
对9Si Cr热轧钢板进行了4种不同工艺的等温球化退火试验,研究了等温温度对钢板球化组织和硬度的影响。结果表明,等温温度过高或过低,都不利于碳化物的球化,等温温度为720℃时
论文部分内容阅读
对9Si Cr热轧钢板进行了4种不同工艺的等温球化退火试验,研究了等温温度对钢板球化组织和硬度的影响。结果表明,等温温度过高或过低,都不利于碳化物的球化,等温温度为720℃时,退火后组织中片状珠光体消失,细小的球状碳化物均匀分布在铁素体基体上,且硬度最低。9Si Cr热轧钢板的等温球化退火温度应是720℃。
The isothermal nodular annealing tests were carried out on 9SiCr hot rolled steel plates in four different processes. The effects of isothermal temperature on the microstructure and hardness of the steel plates were studied. The results show that the isothermal temperature is too high or too low, are not conducive to the carbide ball, the isothermal temperature of 720 ℃, after annealing the flake pearlite disappears, fine spherical carbides uniformly distributed in the ferrite matrix , And the lowest hardness. Isothermal nodular annealing temperature of 9Si Cr hot-rolled steel should be 720 ℃.
其他文献
市场开发被认为是一届奥运会成功与否的重要标志,2008年北京奥运会只剩下五年多时间,北京奥组委这方面的工作进展如何已成为人们关注的热门话题。近日,北京奥组委市场开发部
分别用半导体激光与超音速火焰喷涂设备在45钢基体上制备Ni60合金涂层。用扫描电镜、金相显微镜、XRD对熔覆层进行微观组织和成分的研究。并对熔覆层的显微硬度和耐磨性进行
近读《武当》杂志2003年3期和4期署名“雪僧”先生的《研习丹道应求真务实——评〈丹道法诀十二讲〉》,读后颇觉诧异,如鱼骨在喉,不吐不快,故冒昧提笔阐明观点,以正视听!“
随着新式球拍性能的加强和球手们对网球发球 技术的重视，业余选手也越来越多地面临应付 炮弹式发球的问题。那么应该怎么把这些疾如 炮弹的发球接回去呢？我们首先应该探讨一下
所谓会计资料失真是指企 事业单位财务会计部门 的账目、报表等资料没有按照客观经济活动的实际情况来进行记录和反映,其账目称为假账。在审计中发现,会计资料失真现象越来
1996年10月国际会计准则委员会公布了修订后的国际会计准则第12号——所得税,新准则较1979年发布的准则有一些重要的变化,特别是取消了纳税影响会计法中递延法的使用,这些变
通过金相组织分析研究了X70HD管线钢在两阶段变形后弛豫时间和终冷温度对微观组织的影响。结果表明,第二阶段变形后空冷弛豫到700℃,获得铁素体+下贝氏体的双相组织且无先共
11月16日,商务部合作司负责人介绍了2017年1月~10月我国对外投资合作情况。据统计,1月~10月,我国境内投资者共对全球160个国家和地区的5410家境外企业新增非金融类直接投资,
6月7日,省政协党组召开扩大会议,专题学习毛泽东同志《党委会的工作方法》和习近平总书记重要批示精神。省政协主席、党组书记张连珍主持会议并讲话。张连珍指出,毛泽东同志
采用电化学充氢、慢拉伸试验、TDS分析以及SEM等方法对汽车用590 MPa级别双相钢(DP590)的氢致延迟开裂行为进行研究。结果表明,DP590的氢扩散系数为9.31×10-7cm~2/s。随着充