用Gleeble-3800热模拟试验机研究了850~1050℃温度范围内B对Fe-36Ni因瓦合金热塑性的影响。结果表明,添加0.01%B可显著提高Fe-36Ni因瓦合金的热塑性,尤其是提高850~1000℃温
【机 构】
:
北京科技大学钢铁冶金新技术国家重点实验室,宝钢研究院冶金工艺所,
论文部分内容阅读
用Gleeble-3800热模拟试验机研究了850~1050℃温度范围内B对Fe-36Ni因瓦合金热塑性的影响。结果表明,添加0.01%B可显著提高Fe-36Ni因瓦合金的热塑性,尤其是提高850~1000℃温度范围内的热塑性,断面收缩率均大于80%,拉伸断口均为典型的韧性断裂。热塑性的提高,主要与B元素的晶界偏聚和降低动态结晶开始温度有关。
The influence of B on the thermal plasticity of Fe-36Ni Invar alloy was investigated by Gleeble-3800 thermal simulation test machine at 850 ~ 1050 ℃. The results show that the addition of 0.01% B can significantly improve the thermoplasticity of Fe-36Ni invar. In particular, it increases the thermoplasticity of the Fe-36Ni invar in the temperature range from 850 ℃ to 1000 ℃. The reduction of area is more than 80%. The tensile fracture is a typical ductile fracture. The improvement of the thermostability is mainly related to the segregation of the B element in the grain boundaries and the decrease of the start temperature of the dynamic crystallization.
其他文献
目的:研究抑癌基因p16表达的检测与喉癌组织病理分级的相关性.方法:选择接受喉癌切除术的患者的临床费料,根据术后病理结果判断肿瘤的分化程度及TNM分期,采用Western Blot的
2013年以来,中国进入了“三期叠加”的经济新常态,产生了增长速度换挡、经济结构转型、刺激政策消化等经济问题,为了化解经济新常态下的种种经济问题,党中央提出了供给侧结构
目的 探讨蓝光照射疗法对新生儿黄疸的治疗作用.方法 把在我院因黄疸住院的新生儿56例纳入本研究,将所有患者随机分成试验组和对照组,各28例患者.对照组患儿给予常规治疗,试
以紫铜为焊料,分别在加热时间为10及20 s的两种感应钎焊工艺下,将42CrMo钢与球墨铸铁焊接在一起。对连接后的试样进行860℃×30 min+260℃盐浴处理。利用金相显微镜、显微硬
作为一类综合性的检测技术的化学发光免疫分析技术,其包含了一些检测法的优点,如化学发光检测法、免疫反应检测法等,其中,免疫反应具有较高的灵敏度与特异性.化学发光免疫检
目的 比较综合疗法治疗学龄前儿童各类屈光不正性弱视的疗效.方法 应用综合疗法治疗学龄前儿童屈光不正性弱视856例(1621眼),其中按屈光类型分为远视性弱视1232眼,近视性弱视
目的 总结对比不同时机气管插管在重度颅脑损伤患者治疗中的疗效差别.方法 将我院2009年6月-2011年12月106例中重度颅脑损伤患者随机分为早期插管组(58例)和常规插管组(48例)
选择30例出生2-30d正常分娩的新生婴儿进行为期1个月的抚触按摩,观察生长发育的情况(记录出生第2、15、30天体质量,摄入奶量),结果发现他们的体质量、奶摄入量比非抚触婴儿的
目的:对应用内科治疗消化性溃疡的临床效果进行分析.方法:选取2012年1月至2012年9月我院收治的50例消化性溃疡患者临床资料,所有患者使用奥美拉唑、呋喃唑酮以及克拉霉素三联
在这个科技高速发展的时代,信息化技术在当下的教学中得到了迅猛的发展,但随之也产生了信息化教学的有效性问题,于是乎正视信息化技术在教学中所面临的窘境便成了其研究的目