采用辐照法制备交联聚丙烯酰胺毛细管电泳涂层柱。毛细管先经双功能团试剂γ- 甲基丙烯基氧丙基三甲氧基硅烷预处理,然后柱内充入丙烯酰胺溶液进行辐照聚合,得到线 性涂层柱;再经动态涂覆交联剂甲叉双丙烯酰胺,二次辐照交联,采用随机试验设计方法,对 辐照剂量率、辐照时间和交联剂浓度几个因素进行了优化。在pH 4、333 V/cm场强下,碱性 和酸性蛋白的平均柱效可达9.5 x105和1.69x105理论塔板/米。对不同场强下的柱效、迁移 时间和分高度进行了研究。
Preparation of crosslinked polyacrylamide capillary electrophoresis coated column by irradiation. The capillary was first pretreated with γ-methacryloxypropyltrimethoxysilane by a bifunctional reagent, then the column was filled with an acrylamide solution to conduct irradiation polymerization to obtain a linear coating column; and then a dynamic coating of a crosslinking agent Methylene bisacrylamide, secondary radiation cross-linking, a randomized trial design method, the radiation dose rate, irradiation time and cross-linking agent concentration of several factors were optimized. At pH 4,333 V / cm field strength, the average efficiencies of basic and acidic proteins can reach 9.5 x 105 and 1.69 × 105 theoretical plates per meter. The effects of different field strength, migration time and sub-height were studied.