Fe 3 O 4 nano-whiskers were synthesized via ultrasonic-aided reduction of FeCl 2 ·4H 2 O with N 2 H 4 ·H 2 O in concentrated NaOH solution. Phase identification and morphology observation were conducted by X-ray diffraction (XRD) analysis, transmission electron microscopy (TEM) and field emission scanning electron microscopy (FE-SEM). Face scanning energy dispersive spectrum (face scanning EDS) and two-dimensional fast Fourier transform (2DFFT) for element distribution were carried out for confirming composition homogeneity. From XRD and TEM, the synthesized Fe 3 O 4 nano-whiskers are of cubic phase with average dimension of 20 nm × 200 nm (average aspect ratio of 10). FE-SEM shows that the nano-whiskers without dispersion are interconnected into a network at a scale of 20 m. 2DFFT of the distribution of Fe and O from face scanning EDS confirms the composition homogeneity of the synthesized Fe 3 O 4 . Hydrazine hydrate determines the formation of the nano-whiskers, while the possible mechanism is the preferred growth along certain orientation with the aid of ultrasonic treatment.
Fe 3 O 4 nano-whiskers were synthesized via ultrasonic-aided reduction of FeCl 2 · 4H 2 O with N 2 H 4 · H 2 O in concentrated NaOH solution. Phase identification and morphology observation were conducted by X-ray diffraction (XRD) analysis, transmission electron microscopy (TEM) and field emission scanning electron microscopy (FE-SEM). Face scanning energy dispersive spectrum (face scanning EDS) and two-dimensional fast Fourier transform (2DFFT) for element distribution were carried out for confirming composition homogeneity . From XRD and TEM, the synthesized Fe 3 O 4 nano-whiskers are of cubic phase with an average dimension of 20 nm × 200 nm (average aspect ratio of 10). FE-SEM shows that the nano-whiskers without dispersion are interconnected into a network at a scale of 20 m. 2DFFT of the distribution of Fe and O from face scanning EDS confirms the composition homogeneity of the synthesized Fe 3 O 4. Hydrazine hydrate determines the formation of the nano-whiskers, while the possibl e mechanism is the preferred growth along certain orientation with the aid of ultrasonic treatment.