The effects of rare earth (RE) elements Y and Nd on the microstructure and mechanical properties of Mg-6Al magnesium alloy were investigated. The results show that a proper level of RE elements can obviously refine the microstructure of Mg-6Al magnesium alloys, reduce the quantity of/β-Mg17Al12 phase and form Al2Y and AI2Nd phases. The combined addition of Y and Nd dramatically enhances the tensile strength of the alloys in the temperature range of 20-175℃. When the content of RE elements is up to 1.8%, the values of tensile strength at room temperature and at 150℃ simultaneously reach their maximum of 253 MPa and 196 MPa, respectively.The main mechanisms of enhancement in the mechanical properties of Mg-6Al alloy with Y and Nd are the grain refining strengthening and the dispersion strengthening.