研制出一种能增加水泥石渗透率的增渗剂S-1和KQ-C。S-1是以复杂的天然油溶性有机物为原料自行进行化学改性的固体产物,KQ-C是经过钝化处理的铝粉体系,它可和水泥浆中的碱性物质反应生成氢气的微小气泡,使得原来S-1与S-1不相连的地方,因气泡的产生而相连。并在水泥浆中辅以石英砂、中试纤维、微硅。获得了具有良好浆态性质的防砂用高渗透水泥浆,凝固后的水泥石抗压强度达到7—9MPa。经一定处理后渗透率达到0.5—0.9μm~2。 A penetration enhancer S-1 and KQ-C was developed to increase the permeability of cement stone. S-1 is a solid product chemically modified by a complex natural oil-soluble organic material. KQ-C is a passivated aluminum powder system that reacts with alkaline substances in the slurry to generate a small amount of hydrogen Bubbles, making the original S-1 and S-1 is not connected to the place, due to the generation of bubbles connected. And in the slurry mixed with quartz sand, pilot fiber, micro-silicon. Obtained with good slurry properties of sand with high permeability cement slurry, cement compressive strength reached 7-9MPa. After a certain treatment permeability reached 0.5-0.9μm ~ 2.